Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA PW-978B（粉） TAIWAN CHIMEI
KIBILAC®
Automotive sector、Electrical appliances、Electronic field、Electrical field
High impact resistance、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TAIWAN CHIMEI/PW-978B（粉） |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 9.1E-05 cm/cm/°C |
| Heat Deflection Temperature | Unannealed | ASTMD648 | 93 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 100 °C |
| ASTMD15256 | 113 °C | ||
| Heat Deflection Temperature | 1.8MPa,退火 | ISO75-2/A | 105 °C |
| 1.8MPa,未退火 | ISO75-2/A | 86.0 °C | |
| Vicat Softening Temperature | -- | ISO306/A50 | 112 °C |
| Heat Deflection Temperature | Annealed | ASTMD648 | 103 °C |
| Hardness | Test Condition | Test Method | TAIWAN CHIMEI/PW-978B（粉） |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 105 |
| Physical | Test Condition | Test Method | TAIWAN CHIMEI/PW-978B（粉） |
|---|---|---|---|
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 13 g/10min |
| Modeling Shrinkage | ISO294-4 | 0.40to0.70 % | |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 12.0 cm3/10min |
| Density / Specific Gravity | 23°C | ISO1183 | 1.07 g/cm³ |
| Density/Specific Gravity 2 | ASTMD792 | 1.07 g/cm³ |
| Mechanical Properties | Test Condition | Test Method | TAIWAN CHIMEI/PW-978B（粉） |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2100 Mpa | |
| Tensile Stress | 断裂 | ISO527-2/50 | 34.0 Mpa |
| 屈服 | ISO527-2/50 | 47.0 Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 55 % |
| Flexural Modulus | ASTMD790 | 2260 Mpa | |
| Tensile Strain | 断裂 | ISO527-2/50 | 20 % |
| Flexural Strength | ASTMD790 | 66.3 Mpa | |
| Flexural Stress | ISO178 | 67.0 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 46.0 Mpa |
| Impact Properties | Test Condition | Test Method | TAIWAN CHIMEI/PW-978B（粉） |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C,3.20mm | ASTMD256 | 200 J/m |
| -30°C | ISO180/1A | 5.0 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO179 | 12 kJ/m² |
| -30°C | ISO179 | 6.0 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 12 kJ/m² |
| 23°C,6.40mm | ASTMD256 | 190 J/m |
| Flammability | Test Condition | Test Method | TAIWAN CHIMEI/PW-978B（粉） |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | HB |