ABS 3904 TRINSEO NETHERLANDS
--
--
High impact resistance、Low gloss、 Low gloss、High impact
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | TRINSEO NETHERLANDS/3904 |
|---|---|---|---|
| Melt volume flow rate | 220℃，10KG | ISO 1133 | 4.7 cc/10min |
| melt mass-flow rate | 220℃，10KG | ISO 1133 | 4.7 g/10min |
| Mechanical properties | Test Condition | Test Method | TRINSEO NETHERLANDS/3904 |
|---|---|---|---|
| tensile strength | 屈服,50mm/min | ISO 527 | 37 Mpa |
| elongation | 50mm/min，屈服 | ISO 527 | 2.6 % |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 42 KJ/m |
| Tensile modulus | 1mm/min | ISO 527 | 1820 Mpa |
| tensile strength | 屈服,100mm/min | ISO 527 | 39 Mpa |
| elongation | 100mm/min，屈服 | ISO 527 | 2.8 % |
| Impact strength of cantilever beam gap | -30℃ | ISO 180/1A | 17 KJ/m |
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eA | 18 KJ/m |
| 23℃ | ISO 179/2C(1984) | 22 KJ/m | |
| -30℃ | ISO 179/2C(1984) | 12 KJ/m | |
| bending strength | 2mm/min | ISO 178 | 70 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 37 kJ/m² |
| Flexural modulus | 2mm/min | ISO 178 | 1900 Mpa |
| physical property | Test Condition | Test Method | TRINSEO NETHERLANDS/3904 |
|---|---|---|---|
| Shrinkage rate | 0.4-0.7 % |
| Thermal performance | Test Condition | Test Method | TRINSEO NETHERLANDS/3904 |
|---|---|---|---|
| vicat | 49N/50℃ | ISO 306B | 97 °C |
| Horizontal combustion rate | ISO 3795 | 40 mm/min | |
| UL 94 | HB | ||
| Heat distortion temperature | 1.82MPa，HDT | ISO 75-1 | 97 °C |