PA12 AESNO TL ARKEMA FRANCE
Pebax® Rnew®
Automotive Applications、tubing
UV resistance、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ARKEMA FRANCE/AESNO TL |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| -30°C | ISO 179 | NoBreak |
| Supplementary Information | Test Condition | Test Method | ARKEMA FRANCE/AESNO TL |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA12.EHL.22-010 |
| hardness | Test Condition | Test Method | ARKEMA FRANCE/AESNO TL |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 75 |
| 邵氏D,15秒 | ISO 868 | 69 |
| Mechanical properties | Test Condition | Test Method | ARKEMA FRANCE/AESNO TL |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1440 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | >200 % |
| Flexural modulus | ISO 178 | 1180 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| tensile strength | 断裂 | ASTM D638 | 68.9 Mpa |
| 断裂 | ISO 527-2 | 50.0 Mpa | |
| 屈服 | ISO 527-2 | 43.0 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 140 J/m | |
| elongation at break | ASTM D638 | 330 % | |
| Flexural modulus | ASTM D790 | 1200 Mpa |
| flammability | Test Condition | Test Method | ARKEMA FRANCE/AESNO TL |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ARKEMA FRANCE/AESNO TL |
|---|---|---|---|
| Shore hardness | ASTM 785 | 106 | |
| Melt volume flow rate | 235°C/5.0kg | ISO 11357 | 8.00 cm3/10min |
| Water absorption rate | 23℃，50%RH | ASTM D570 | 0.80 % |
| Thermal performance | Test Condition | Test Method | ARKEMA FRANCE/AESNO TL |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 180 °C | |
| Glass Transition Temperature | ASTM E1356 | 35.0 °C |