Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A705R-V0 宁波德立隆
--
阻燃性,耐热性,电阻性良好
接插件,电子端子,电子元件等
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 宁波德立隆/A705R-V0 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 9 kJ/m² | |
| Rockwell hardness | R标尺 | 120 | |
| Simple support without notch impact strength | ISO 179/1eU | 27 kJ/m² | |
| bending strength | ISO 178 | 180 Mpa | |
| elongation at break | ISO 527 | 3 | |
| Flexural modulus | ISO 178 | 7000 Mpa | |
| Tensile strength at break | ISO 527 | 120 Mpa |
| other | Test Condition | Test Method | 宁波德立隆/A705R-V0 |
|---|---|---|---|
| Drying temperature/time | 90/6-10 °C/hr | ||
| Injection molding temperature range | 260-285 °C | ||
| Surface Resistivity | ISO 167 | 10¹³ Ohm | |
| Linear forming shrinkage rate | ISO 2577 | 0.003 mm/mm | |
| dielectric strength | IEC 1183 | 19 KV/mm | |
| filler | GF30 % |
| Flame retardant performance | Test Condition | Test Method | 宁波德立隆/A705R-V0 |
|---|---|---|---|
| Flame retardant grade | UL94 | V-0 |
| physical property | Test Condition | Test Method | 宁波德立隆/A705R-V0 |
|---|---|---|---|
| Water absorption rate | 24hr，23°C | ISO 62 | 0.6 % |
| density | ISO 1183 | 1.46 g/cm³ |
| Thermal performance | Test Condition | Test Method | 宁波德立隆/A705R-V0 |
|---|---|---|---|
| Heat distortion temperature | 1.82MPa | ISO 75 | 240 ℃ |
| 0.45MPa | ISO 75 | 250 ℃ |