Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1621-02 LG CHEM KOREA
LUPOY®
bottle,Non specific food
heat-resisting,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/1621-02 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ISO 180 | 930 J/m |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| thermal performance | Test Condition | Test Method | LG CHEM KOREA/1621-02 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Annealed，HDT | ISO 75-2/B | 142 °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 128 °C |
| vicat | ISO 306/B50 | 146 °C | |
| Heat Deflection Temperature | 1.8MPa,Annealed，HDT | ISO 75-2/A | 137 °C |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/1621-02 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2280 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 63.0 Mpa |
| 断裂 | ISO 527-2 | 60.0 Mpa | |
| bending strength | ISO 178 | 96.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 90 % |
| 屈服 | ISO 527-2 | 6.0 % | |
| flexural modulus | ISO 178 | 2410 Mpa |
| optical performance | Test Condition | Test Method | LG CHEM KOREA/1621-02 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 0.70to1.5 % |
| Physical properties | Test Condition | Test Method | LG CHEM KOREA/1621-02 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| 23°C,24hr | ASTM D570 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 2.5 g/10min |
| shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |