Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 2034 SABIC INNOVATIVE NETHERLANDS
LEXAN™
Lighting applications、Plastic bag
Middle flow、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 100 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.70 |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.70 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 27 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| relative permittivity | 1MHz | IEC 60250 | 2.70 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| 60Hz | IEC 60250 | 1E-03 | |
| 1MHz | IEC 60250 | 0.010 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| bending strength | ISO 178 | 95.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 9.00 mg |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 70.0 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | <0.80 % |
| refractive index | ISO 489 | 1.586 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0to90.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | V-0 |
| Burning wire flammability index | 1.8mm | IEC 60695-2-12 | 960 °C |
| 1.0mm | IEC 60695-2-12 | 850 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| Limiting Oxygen Index | ISO 4589-2 | 40 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 8.50 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.13 % |
| 饱和,23°C | ISO 62 | 0.32 % | |
| Shrinkage rate | MD3 | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/2034 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距，HDT | ISO 75-2/Ae | 129 °C |
| ball-indentation hardness | 140°C9 | IEC 60695-10-2 | 通过 |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| vicat | -- | ISO 306/B120 | 145 °C |
| Heat distortion temperature | 0.45MPa,未退火,100mm跨距，HDT | ISO 75-2/Be | 140 °C |
| vicat | -- | ISO 306/B50 | 144 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |