Product Name / Manufacturer / Model

Brand

Typical Applications

Properties

Color

Form

Processing Methods

Grade

Filler

Recycled Content

Certificates

Reference Price

PBT
PBT DUPONT USA SK605-NC010
Enhanced level
UL
US$ 3,530 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodDUPONT USA/SK605-NC010
bending strengthISO 178200 Mpa
Tensile creep modulus1hrISO 899-19000 Mpa
compressive strength5 mm/min, 3.20 mm, 23 ℃ASTM D695202 MPa
Impact strength of cantilever beam gap23℃ASTM D256112 J/m
Elongation at Break23℃ASTM D6382.6 %
Tensile strainBreakISO 527-22.7 %
Tensile modulusISO 527-210000 Mpa
Bending modulusISO 1789000 Mpa
Tensile creep modulus1000hrISO 899-16600 Mpa
Bending modulus23℃ASTM D7908970 MPa
Suspended wall beam without notch impact strength23℃ASTM D256998 J/m
tensile strengthBreakISO 527-2140 Mpa
Tensile modulus23℃ASTM D63810000 MPa
Suspended wall beam without notch impact strength-40℃ASTM D2561120 J/m
Impact strength of cantilever beam gap-40℃ASTM D256101 J/m
ASTM D256101 J/m
tensile strength23℃ASTM D638140 MPa
flammabilityTest ConditionTest MethodDUPONT USA/SK605-NC010
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
Extreme Oxygen IndexISO 4589-219 %
UL flame retardant rating1.5mmUL 94HB
0.75mmIEC 60695-11-10,-20HB
0.75mmUL 94HB
Atomizationrefraction，F值ISO 645299 %
Burning rate1.00mmISO 379541 mm/min
FMVSS flammabilityFMVSS302B
Physical propertiesTest ConditionTest MethodDUPONT USA/SK605-NC010
densityISO 11831.53 g/cm³
Shrinkage rateMDISO 294-40.30 %
Water absorption rateSaturation,23°C,2.00mmISO 620.35 %
Top out temperature170 °C
SpecificHeatCapacity of Melt1730 J/kg/°C
Shrinkage rateTDISO 294-41.1 %
MediumDensity1.36 g/cm³
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.15 %
densityASTM D7921.53
ThermalConductivityofMelt0.28 W/m/K
melt mass-flow rateISO 113310 g/10min
Melt Volume Flow Rate (MVR)250°C/2.16kgISO 11337.00 cm3/10min
StickinessISO 307100 cm³/g
Electrical performanceTest ConditionTest MethodDUPONT USA/SK605-NC010
Dissipation factor100HzIEC 602507.5E-04
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dissipation factor1MHzIEC 602500.018
Relative permittivity100HzIEC 602503.90
Surface resistivityIEC 60093>1.0E+15 ohms
Relative permittivity1MHzIEC 602503.80
Dielectric strengthIEC 60243-138 KV/mm
Compared to the anti leakage trace indexIEC 60112PLC 1
impact performanceTest ConditionTest MethodDUPONT USA/SK605-NC010
Suspended wall beam without notch impact strength-40°CISO 180/1U55 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU75 kJ/m²
Charpy Notched Impact Strength-40°CISO 179/1eA10 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U60 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA11 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A11 kJ/m²
-40°CISO 180/1A10 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU70 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U55 kJ/m²
Impact strength of simply supported beam without notch-40°CISO 179/1eU75 kJ/m²
Supplementary InformationTest ConditionTest MethodDUPONT USA/SK605-NC010
OdorVDA2703.00
EmissionofOrganicCompoundsVDA277140 µgC/g
thermal performanceTest ConditionTest MethodDUPONT USA/SK605-NC010
Linear coefficient of thermal expansion平行Flow，73 to 130°F (23 to 55℃)ASTM E8310.000030 cm/cm/℃
UL flame retardant rating3.00 mmUL 94HB
1.50 mmUL 94HB
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A205 °C
Melting temperatureISO 11357-3224 °C
Vicat softening temperatureISO 306/B50215 °C
Linear coefficient of thermal expansion垂直Flow，73 to 130°F (23 to 55℃)ASTM E8310.000090 cm/cm/℃
MDISO 11359-23E-05 cm/cm/°C
Hot deformation temperature0.45Mpa,UnannealedASTM D648220 ℃
0.45MPa,UnannealedISO 75-2/B220 °C
Linear coefficient of thermal expansionTDISO 11359-29E-05 cm/cm/°C
Hot deformation temperature1.8Mpa,UnannealedASTM D648205 ℃
UL flame retardant rating0.750 mmUL 94HB
Other performanceTest ConditionTest MethodDUPONT USA/SK605-NC010
Extreme Oxygen IndexASTM D286319 %

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China