PC 8430-7 STYRON TAIWAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | STYRON TAIWAN/8430-7 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 17 KV/mm | |
| dielectric constant | 50Hz | IEC 60250 | 2.70 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1Hz | IEC 60250 | 1E-03 |
| dielectric constant | 1Hz | IEC 60250 | 2.70 |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| Mechanical properties | Test Condition | Test Method | STYRON TAIWAN/8430-7 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| bending strength | ISO 178 | 95.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 110 % |
| Flexural modulus | ISO 178 | 2350 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| tensile strength | 断裂 | ISO 527-2 | 70.0 Mpa |
| 屈服 | ISO 527-2 | 60.0 Mpa |
| optical performance | Test Condition | Test Method | STYRON TAIWAN/8430-7 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 88.0to89.0 % |
| flammability | Test Condition | Test Method | STYRON TAIWAN/8430-7 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm3 | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 800 °C |
| 1.0mm | IEC 60695-2-13 | 800 °C | |
| Burning wire flammability index | 1.0mm4 | IEC 60695-2-12 | 960 °C |
| 3.0mm3 | IEC 60695-2-12 | 960 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 40 % | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | STYRON TAIWAN/8430-7 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.50-0.70 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON TAIWAN/8430-7 |
|---|---|---|---|
| Ball pressure temperature | IEC 60335-1 | >125 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 141 °C |
| vicat | ISO 306/B50 | 148 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 125 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 144 °C |