| hardness | Test Condition | Test Method | STYRON US/301 BK |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 118 |
| M计秤 | ISO 2039-2 | 73 |
| Mechanical properties | Test Condition | Test Method | STYRON US/301 BK |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| Tensile modulus | ISO 527-2/50 | 2300 Mpa | |
| bending strength | ISO 178 | 97.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 150 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| Taber abraser | ISO 9352 | 45 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 71.0 Mpa |
| Electrical performance | Test Condition | Test Method | STYRON US/301 BK |
|---|---|---|---|
| dielectric constant | 60Hz | IEC 60250 | 3.00 |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm,SolutionA | IEC 60112 | PLC 2 |
| dielectric strength | IEC 60243-1 | 17 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.00 |
| dielectric constant | 1MHz | IEC 60250 | 3.00 |
| relative permittivity | 1MHz | IEC 60250 | 3.00 |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| 1MHz | IEC 60250 | 2E-03 |
| optical performance | Test Condition | Test Method | STYRON US/301 BK |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| Haze ratio | ASTM D1003 | 1.0 % | |
| refractive index | ISO 489 | 1.586 |
| flammability | Test Condition | Test Method | STYRON US/301 BK |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 875 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
| 1.0mm | IEC 60695-2-13 | 800 °C | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 900 °C |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 875 °C |
| physical property | Test Condition | Test Method | STYRON US/301 BK |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.15 % |
| Melt volume flow rate | 300°C/1.2kg | ASTM D1505 | 14.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.32 % |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/301 BK |
|---|---|---|---|
| Ball pressure temperature | IEC 60335-1 | >125 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 140 °C |
| vicat | ISO 306/B50 | 148 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 124 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 143 °C |