Certificates
PP Fiberfil® J-60/20/E8/M Canada Fiberfil
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/20/E8/M |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 64 J/m |
| hardness | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/20/E8/M |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 100to110 |
| Mechanical properties | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/20/E8/M |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 93.1 MPa |
| tensile strength | 23°C | ASTM D638 | 68.9 MPa |
| Tensile modulus | 23°C | ASTM D638 | 4140 MPa |
| Flexural modulus | 23°C | ASTM D790 | 3790 MPa |
| elongation | 屈服,23°C | ASTM D638 | 3.5 % |
| physical property | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/20/E8/M |
|---|---|---|---|
| Shrinkage rate | MD：6.35mm | ASTM D955 | 0.40 % |
| Water absorption rate | 24hr | ASTM D570 | 0.030 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 9.0 g/10min |
| density | ASTM D792 | 1.04 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.30 % |
| Thermal performance | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/20/E8/M |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 149 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 157 °C |