LCP A150 JAPAN POLYPLASTIC
LAPEROS®
Home appliance components、Electrical applications
enhance、Glass fiber reinforced、Flame retardant、Halogen-free
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 90 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| ColorNumber | VF2001/BK210P |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 260 kg/cm²(MPa)[Lb/in²] | |
| elongation | 断裂 | ASTM D638 | 1.5 % |
| Flexural modulus | ASTM D790/ISO 178 | 20500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 260 Mpa | |
| Flexural modulus | ISO 178 | 20500 Mpa | |
| Bending Strain | ISO 178 | 1.8 % | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 180 kg/cm²(MPa)[Lb/in²] | |
| ASTM D638 | 180 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| relative permittivity | 1kHz | IEC 60250 | 4.50 |
| dielectric strength | 1.00mm | IEC 60243-1 | 44 KV/mm |
| Dissipation Factor | 耐电弧性 | IEC 60250 | 180 sec |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric constant | ASTM D150/IEC 60250 | 4.1 | |
| dielectric strength | 3.00mm | IEC 60243-1 | 28 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 4.10 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| other | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| characteristic | 玻璃纤维. 高刚性 | ||
| Color | VF2001/BK210P |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.81 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| Shrinkage rate | TD:1.00mm | 内部方法 | 0.40 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Shrinkage rate | MD:1.00mm | 内部方法 | 0.11 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/A150 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 240 °C |