LDPE+EVA Trademark PE LDVA2925.3B Trademark Plastics Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LDVA2925.3B |
|---|---|---|---|
| elongation | MD:断裂,38µm,吹塑薄膜 | ASTM D882 | 340 % |
| Secant modulus | 1%正割,TD:38µm,吹塑薄膜 | ASTM D882 | 169 MPa |
| tensile strength | MD:断裂,38µm,吹塑薄膜 | ASTM D882 | 22.1 MPa |
| film thickness | 38 µm | ||
| Elmendorf tear strength | TD:38µm,吹塑薄膜 | ASTM D1922 | 110 g |
| elongation | TD:断裂,38µm,吹塑薄膜 | ASTM D882 | 540 % |
| Dart impact | 38µm,吹塑薄膜 | ASTM D1709 | 120 g |
| Elmendorf tear strength | MD:38µm,吹塑薄膜 | ASTM D1922 | 210 g |
| tensile strength | TD:断裂,38µm,吹塑薄膜 | ASTM D882 | 16.9 MPa |
| Secant modulus | 1%正割,MD:38µm,吹塑薄膜 | ASTM D882 | 141 MPa |
| optical performance | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LDVA2925.3B |
|---|---|---|---|
| Haze ratio | 38.1µm,吹塑薄膜 | ASTM D1003 | 5.0 % |
| gloss | 45°,38.1µm,吹塑薄膜 | ASTM D2457 | 76 |
| physical property | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LDVA2925.3B |
|---|---|---|---|
| density | ASTM D1505 | 0.925 g/cm³ | |
| Vinyl acetate content | 2.5 wt% | ||
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.5 g/10min |