Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PP K8003 SECCO SHANGHAI
--
Automotive sector
High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Other performance | Test Condition | Test Method | SECCO SHANGHAI/K8003 |
---|---|---|---|
Huangdu Index | ASTM D-192563T | 2 % |
Basic Performance | Test Condition | Test Method | SECCO SHANGHAI/K8003 |
---|---|---|---|
density | ASTM D-1505 | 0.90 g/cm³ | |
melt mass-flow rate | ASTM D-1238 | 2.50 g/10min |
thermal performance | Test Condition | Test Method | SECCO SHANGHAI/K8003 |
---|---|---|---|
Hot deformation temperature | 0.46MPa | ASTM D-648 | 93 °C |
Vicat softening temperature | ASTM D1525/ISO R306 | 65 ℃(℉) |
mechanical properties | Test Condition | Test Method | SECCO SHANGHAI/K8003 |
---|---|---|---|
Bending modulus | ASTM D-790A | 1300 Mpa | |
ASTM D790/ISO 178 | 970 kg/cm²(MPa)[Lb/in²] | ||
elongation | Break | ASTM D-638 | >200 % |
Elongation at Break | ASTM D638/ISO 527 | 》200 % | |
Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | NB J/m |
-20℃ | ASTM D-256 | 70 J/m | |
Rockwell hardness | ASTM D-785 | 75 R-Scale | |
ASTM D785 | 86 | ||
tensile strength | ASTM D638/ISO 527 | 23 kg/cm²(MPa)[Lb/in²] | |
Yield | ASTM D-638 | 26.0 Mpa |
other | Test Condition | Test Method | SECCO SHANGHAI/K8003 |
---|---|---|---|
characteristic | 通用型 |
Physical properties | Test Condition | Test Method | SECCO SHANGHAI/K8003 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 0.093 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | 2.5 g/10min |