PC/ABS LDS3720 MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Shell,Electronic and Electrical Applications
heat-resisting,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS3720
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A102 °C
Linear coefficient of thermal expansionTDISO 11359-27E-05 cm/cm/°C
MDISO 11359-27E-05 cm/cm/°C
Vicat softening temperatureISO 306/B50122 °C
mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS3720
Bending modulusISO 1782250 Mpa
bending strengthISO 17880.0 Mpa
Nominal tensile fracture strainISO 527-2>50 %
Tensile modulusISO 527-22250 Mpa
Tensile strainYieldISO 527-24.0 %
tensile strengthYieldISO 527-251.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS3720
Dielectric constant1.00GHzIEC 602502.80
Dissipation factorIEC 602505E-03
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Physical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS3720
Melt Volume Flow Rate (MVR)260°C/5.0kgISO 113313.0 cm3/10min
Shrinkage rateISO 294-40.60 %
Water absorption rateSaturation,23°CISO 620.60 %
impact performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS3720
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
23°CISO 179/1eUNoBreak
Multi axis Instrumented Impact Energy23°C2Internal Method25.0 J
23°CISO 6603-235.0 J
-20°C2Internal Method10.0 J
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/LDS3720
UL flame retardant rating0.70mmIEC 60695-11-10,-20HB
1.5mmUL 94HB