Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 203-40 CELANESE USA
Santoprene™
Electrical components、diaphragm、Pipe fittings、Movable hinge、Home appliance components、Engine hood parts、Automotive sector、Consumer goods sector、Pipe fittings、diaphragm、Movable hinge、Consumer product applicat、Parts under the hood of a、Application in the automo、Electrical components、Home appliance components
dimensional stability 、Insulation performance、Recyclable materials、Electrical performance、Superior tear strength、Good colorability、Ozone resistance、Chemical resistance、Fatigue resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/203-40 |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒,23°C | ISO 868 | 41 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/203-40 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| dielectric strength | 23°C,2.00mm | ASTM D149 | 28 KV/mm |
| Hot wire ignition (HWI) | 1.0mm | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 3 |
| 3.0mm | UL 746 | PLC 2 | |
| dielectric constant | 23°C,1.98mm | IEC 60250 | 2.30 |
| 23°C,1.98mm | ASTM D150 | 2.30 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 |
| flammability | Test Condition | Test Method | CELANESE USA/203-40 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| elastomer | Test Condition | Test Method | CELANESE USA/203-40 |
|---|---|---|---|
| elongation | 断裂,23°C，横向 | ASTM D412 | 610 % |
| Tensile stress | 100%应变,23°C，横向流量 | ISO 37 | 9.00 Mpa |
| tensile strength | 断裂,23°C，横向流量 | ASTM D412 | 20.7 Mpa |
| elongation | 断裂,23°C，横向 | ISO 37 | 610 % |
| tear strength | 23°C，Across Flow (横向) | ISO 34-1 | 67 kN/m |
| tensile strength | Break,23°C | ISO 37 | 20.7 Mpa |
| compression set | 70°C,22hr | ASTM D395B | 54 % |
| 70°C,22hr | ISO 815 | 54 % | |
| 125°C,70hr | ISO 815 | 61 % | |
| tear strength | 23°C，横向流量 | ASTM D624 | 67.0 kN/m |
| compression set | 125°C,70hr | ASTM D395B | 61 % |
| Tensile stress | 100%应变,23°C，横向流量 | ASTM D412 | 9.00 Mpa |
| aging | Test Condition | Test Method | CELANESE USA/203-40 |
|---|---|---|---|
| mass change fraction | 23°C,168hr,inMethylethylketone | ASTM D471 | -12 % |
| Tensile stress change rate | 23°C,168hr,inIsopropylAlcohol，断裂 | ISO 1817 | 5.0 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 1.0 |
| Change rate of tensile strength in air | 23°C,168hr,inIsopropylAlcohol | ISO 1817 | 5.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 2.0 |
| ShoreA,23°C,168hr,inSodiumChloride,15% | ASTM D471 | 2.0 | |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 2.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inAceticAcid | ISO 1817 | 0.0 % |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 4.0 % | |
| Shore hardness | ShoreA,100°C,168hr,inDeionizedWater | ISO 1817 | 0.0 |
| mass change fraction | 23°C,168hr,inCyclohexane | ASTM D471 | -3.4 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | -0.60 % | |
| Change rate of tensile strength in air | 125°C,168hr,inIRM903Oil | ASTM D471 | -30 % |
| 125°C,168hr,inIRM903Oil | ISO 1817 | -30 % | |
| mass change fraction | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.0 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumChloride,15% | ISO 1817 | 2.0 |
| Change rate of hardness (Shore) in the air | ShoreA,125°C,168hr,inIRM903Oil | ASTM D471 | -15 |
| mass change fraction | 23.0°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.10 % |
| Tensile stress change rate | 23°C,168hr,inSulfuricAcid,98%，断裂 | ISO 1817 | -23 % |
| mass change fraction | 23°C,168hr,inTrichloroethylene | ASTM D471 | -1.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 6.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inMethylethylketone | ASTM D471 | 0.0 |
| Change rate of tensile strength in air | 150°C,168hr | ISO 188 | -11 % |
| Tensile stress change rate | 125°C,70hr,inIRM903Oil，断裂 | ISO 1817 | -33 % |
| Shore hardness | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ISO 1817 | 0.0 |
| Change rate of tensile strength in air | 100°C,168hr,inIRM903Oil | ISO 1817 | -26 % |
| Tensile stress change rate | 100°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -28 % |
| mass change fraction | 100°C,168hr,inIRM903Oil | ASTM D471 | 35 % |
| 23.0°C,168hr,inTrichloroethylene | ISO 1817 | -1.0 % | |
| Change rate of tensile strength in air | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | 5.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inTrichloroethylene | ASTM D471 | 1.0 |
| mass change fraction | 23.0°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 0.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inEthanol,95% | ASTM D471 | 0.0 |
| Shore hardness | ShoreA,23°C,168hr,inEthanol,95% | ISO 1817 | 0.0 |
| ShoreA,125°C,168hr,inIRM903Oil | ISO 1817 | -15 | |
| Change rate of tensile strength in air | 100°C,168hr,inDeionizedWater | ISO 1817 | 3.0 % |
| Change rate of ultimate elongation in air | 100°C,168hr,inIRM903Oil | ASTM D471 | -28 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | -2.0 % | |
| volume change | 125°C,70hr,在IRM903油中 | ASTM D471 | 40 % |
| Shore hardness | ShoreA,23°C,168hr,inAceticAcid | ISO 1817 | -1.0 |
| Change rate of ultimate elongation in air | 150°C,168hr | ASTM D573 | -15 % |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr,inIRM903Oil | ASTM D471 | -13 |
| mass change fraction | 23.0°C,168hr,inMethylethylketone | ISO 1817 | -12 % |
| Change rate of tensile strength in air | 23°C,168hr,inMethylethylketone | ASTM D471 | 3.0 % |
| 23°C,168hr,inSulfuricAcid,98% | ISO 1817 | -22 % | |
| 23°C,168hr,inDetergent(Tide),2.5% | ISO 1817 | 0.0 % | |
| 125°C,70hr,inIRM903Oil | ISO 1817 | -27 % | |
| Tensile stress change rate | 23°C,168hr,inTrichloroethylene，断裂 | ISO 1817 | 2.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inMethylethylketone | ASTM D471 | 2.0 % |
| mass change fraction | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.10 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 4.0 % |
| 23°C,168hr,inAceticAcid | ASTM D471 | 0.0 % | |
| Tensile stress change rate | 125°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -39 % |
| Shore hardness | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -1.0 |
| ShoreA,100°C,168hr,inIRM903Oil | ISO 1817 | -13 | |
| Change rate of tensile strength in air | 23°C,168hr,inTrichloroethylene | ASTM D471 | 8.0 % |
| volume change | 125°C,70hr,在IRM903油中 | ISO 1817 | 40 % |
| Shore hardness | ShoreA,23°C,168hr,inIsopropylAlcohol | ISO 1817 | 2.0 |
| ShoreD,150°C,168hr | ISO 188 | 4.0 | |
| Tensile stress change rate | 100°C,168hr,inDeionizedWater，断裂 | ISO 1817 | 0.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 5.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 1.0 |
| Change rate of tensile strength in air | 150°C,168hr | ASTM D573 | -11 % |
| Tensile stress change rate | 23°C,168hr,inSodiumChloride,15%，断裂 | ISO 1817 | 2.0 % |
| mass change fraction | 23°C,168hr,inAceticAcid | ASTM D471 | 1.2 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | 5.0 % |
| mass change fraction | 23.0°C,168hr,inAceticAcid | ISO 1817 | 1.2 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -1.0 |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 6.0 % |
| Tensile stress change rate | 23°C,168hr,inDetergent(Tide),2.5%，断裂 | ISO 1817 | 0.00.0 % |
| Change rate of ultimate elongation in air | 125°C,168hr,inIRM903Oil | ASTM D471 | -39 % |
| Tensile stress change rate | 23°C,168hr,inEthanol,95%，断裂 | ISO 1817 | -2.0 % |
| 23°C,168hr,inCyclohexane，断裂 | ISO 1817 | 2.0 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inTrichloroethylene | ASTM D471 | 2.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inTrichloroethylene | ISO 1817 | 8.0 % |
| Shore hardness | ShoreA,23°C,168hr,inMethylethylketone | ISO 1817 | 0.0 |
| mass change fraction | 125°C,168hr,inIRM903Oil | ISO 1817 | 44 % |
| Change rate of tensile strength in air | 23°C,168hr,inCyclohexane | ASTM D471 | -2.0 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | -3.0 % | |
| 100°C,168hr,inDeionizedWater | ASTM D471 | 3.0 % | |
| mass change fraction | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 1.1 % |
| Change rate of tensile strength in air | 100°C,168hr,inIRM903Oil | ASTM D471 | -26 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inCyclohexane | ASTM D471 | 2.0 % |
| Tensile stress change rate | 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | 3.0 % |
| Change rate of ultimate elongation in air | 100°C,168hr,inDeionizedWater | ASTM D471 | 0.0 % |
| mass change fraction | 23.0°C,168hr,inIsopropylAlcohol | ISO 1817 | -5.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 0.00.0 % |
| mass change fraction | 23.0°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 0.10 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumChloride,15% | ISO 1817 | 4.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 0.0 |
| Tensile stress change rate | 23°C,168hr,inHydrochloricAcid,10%，断裂 | ISO 1817 | 5.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inCyclohexane | ISO 1817 | -2.0 % |
| mass change fraction | 23.0°C,168hr,inCyclohexane | ISO 1817 | -3.4 % |
| Change rate of tensile strength in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | -22 % |
| mass change fraction | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | -5.0 % |
| Hardness change rate in the air | ShoreD,150°C,168hr | ASTM D573 | 4.0 |
| mass change fraction | 23.0°C,168hr,inSulfuricAcid,98% | ISO 1817 | 1.1 % |
| Shore hardness | ShoreA,23°C,168hr,inSulfuricAcid,98% | ISO 1817 | 2.0 |
| mass change fraction | 100°C,168hr,inIRM903Oil | ISO 1817 | 35 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 4.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 3.0 % |
| mass change fraction | 100°C,168hr,inDeionizedWater | ASTM D471 | 1.4 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | -23 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inAceticAcid | ASTM D471 | -1.0 |
| ShoreA,23°C,168hr,inIsopropylAlcohol | ASTM D471 | 2.0 | |
| Change rate of ultimate elongation in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -33 % |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr,inDeionizedWater | ASTM D471 | 0.0 |
| Change rate of tensile strength in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -27 % |
| mass change fraction | 23.0°C,168hr,inEthanol,95% | ISO 1817 | -0.60 % |
| Shore hardness | ShoreA,23°C,168hr,inTrichloroethylene | ISO 1817 | 1.0 |
| Tensile stress change rate | 23°C,168hr,inMethylethylketone，断裂 | ISO 1817 | 2.0 % |
| mass change fraction | 100°C,168hr,inDeionizedWater | ISO 1817 | 1.4 % |
| Shore hardness | ShoreA,23°C,168hr,inCyclohexane | ISO 1817 | -13 |
| mass change fraction | 125°C,168hr,inIRM903Oil | ASTM D471 | 44 % |
| Change rate of tensile strength in air | 23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 0.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inCyclohexane | ASTM D471 | -13 |
| Change rate of tensile strength in air | 23°C,168hr,inMethylethylketone | ISO 1817 | 3.0 % |
| mass change fraction | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.10 % |
| Change rate of tensile strength in air | 23°C,168hr,inEthanol,95% | ISO 1817 | -3.0 % |
| physical property | Test Condition | Test Method | CELANESE USA/203-40 |
|---|---|---|---|
| Resistance to cleaning agents | UL 749 | f3 | |
| ISO 188 | f4 |
| Thermal performance | Test Condition | Test Method | CELANESE USA/203-40 |
|---|---|---|---|
| brittle temperature | ISO 812 | -52.0 °C | |
| ASTM D746 | -52.0 °C | ||
| RTI Str | UL 746 | 85.0 °C | |
| RTI Elec | UL 746 | 85.0 °C |