Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC TRISTAR® PC-10R-(IM) PTS USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PTS USA/TRISTAR® PC-10R-(IM) |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.17mm | ASTM D256 | 800 J/m |
| hardness | Test Condition | Test Method | PTS USA/TRISTAR® PC-10R-(IM) |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | PTS USA/TRISTAR® PC-10R-(IM) |
|---|---|---|---|
| Hot wire ignition (HWI) | 3.00mm | UL 746 | PLC 1 sec |
| 1.50mm | UL 746 | PLC 2 sec | |
| 1.5mm | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | 60.0to120 sec | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 3.00mm | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 mm/min |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.50mm | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | PTS USA/TRISTAR® PC-10R-(IM) |
|---|---|---|---|
| Flexural modulus | 3.17mm | ASTM D790 | 2070 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 55.2 MPa |
| bending strength | 屈服,3.17mm | ASTM D790 | 86.2 MPa |
| elongation | 断裂,3.17mm | ASTM D638 | 110 % |
| flammability | Test Condition | Test Method | PTS USA/TRISTAR® PC-10R-(IM) |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | PTS USA/TRISTAR® PC-10R-(IM) |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | PTS USA/TRISTAR® PC-10R-(IM) |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 127 °C |
| Linear coefficient of thermal expansion | TD:-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 137 °C |
| Linear coefficient of thermal expansion | MD:-40到95°C | ASTME831 | 7E-05 cm/cm/°C |
| RTI Imp | UL 746 | 115 °C | |
| RTI | UL 746 | 125 °C | |
| RTI Elec | UL 746 | 125 °C |