Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM M270 TAIWAN POLYPLASTICS
DURACON®
Household appliances、Household appliances、Automotive sector
Low molecular weight、Good forming performance、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.3 kJ/m² |
| hardness | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 80 |
| Supplementary Information | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| ColorNumber | CF2001 |
| Mechanical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 30 % | |
| Tensile stress | ISO527-2 | 63.0 Mpa | |
| Bending stress | ISO178 | 88.0 Mpa | |
| Flexural modulus | ISO178 | 2550 Mpa |
| Electrical performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| CTI | IEC60112 | >600 V | |
| dielectric strength | 3.00mm | IEC60243-1 | 19 KV/mm |
| flammability | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 27 g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 23.0 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 % |
| density | ISO1183 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/M270 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/A | 100 °C | |
| TD:23到55°C | 内部方法 | 1.1E-04 cm/cm/°C | |
| MD:23到55°C | 内部方法 | 1.1E-04 cm/cm/°C |