POM LT350 ASAHI JAPAN
TENAC™-C
Electrical field、Electronic field、Industrial applications、Automotive sector、Shell、Engineering accessories、Engine parts
copolymer、wear resistant、high viscosity、Low friction coefficient、High lubrication
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/LT350 |
---|---|---|---|
Tensile modulus | ISO 527-2 | 2500 Mpa | |
elongation | 断裂 | ASTMD638 | 45 % |
tensile strength | -- | ASTM D638 | 56.0 Mpa |
bending strength | ASTM D790 | 78.0 Mpa | |
Flexural modulus | -- | ISO 178 | 2300 Mpa |
tensile strength | 屈服 | ISO 527-2 | 58.0 Mpa |
Flexural modulus | -- | ASTM D790 | 2350 Mpa |
other | Test Condition | Test Method | ASAHI JAPAN/LT350 |
---|---|---|---|
characteristic | 高冲击强度 良好的耐摩擦和磨耗性 | ||
purpose | 办公室仪器的轴承.齿轮 车辆配件 |
flammability | Test Condition | Test Method | ASAHI JAPAN/LT350 |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | ASAHI JAPAN/LT350 |
---|---|---|---|
Shrinkage rate | MD | 内部方法 | 1.6-2.0 % |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.0 g/10min |
Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
Thermal performance | Test Condition | Test Method | ASAHI JAPAN/LT350 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 152 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 85.0 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |