ASA S310 UMG JAPAN
DIALAC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/S310 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 103 |
| Basic performance | Test Condition | Test Method | UMG JAPAN/S310 |
|---|---|---|---|
| melt mass-flow rate | 20 CM |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/S310 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 65.0 Mpa |
| Flexural modulus | 2300 Mpa | ||
| 23°C | ISO 178 | 2300 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 2100 Mpa |
| Charpy Notched Impact Strength | 18 KJ/m | ||
| tensile strength | 23°C | ISO 527-2 | 41.0 Mpa |
| flammability | Test Condition | Test Method | UMG JAPAN/S310 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | UMG JAPAN/S310 |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.40-0.60 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 20.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/S310 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 81.0 °C |
| HDT | 81 °C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| UL flame retardant rating | UL 94 | HB |