Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 6015S-04 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/6015S-04 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 15 kJ/m² |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6015S-04 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| relative permittivity | 10kHz | IEC 60250 | 2.35 |
| 1kHz | IEC 60250 | 2.35 | |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| Dissipation Factor | 1.00GHz | IEC 60250 | 7E-05 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6015S-04 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 2.5 % |
| Tensile modulus | ISO 527-2/1A/1 | 3000 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 60.0 Mpa |
| optical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6015S-04 |
|---|---|---|---|
| transmissivity | ISO 13468-2 | 91.0 % | |
| refractive index | ISO 489 | 1.530 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/6015S-04 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/6015S-04 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.50-0.70 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 4.00 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.010 % |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 3.7 g/10min |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6015S-04 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 150 °C |
| vicat | ISO 306/B50 | 156 °C | |
| Glass Transition Temperature | ISO 11357-2 | 158 °C |