Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GSH2020LR Y083 MITSUBISHI GAS SHANGHAI
IUPILON™
Automotive components、Special for cast film、Camera applications
High temperature resistan、wear resistant、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI GAS SHANGHAI/GSH2020LR Y083 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI GAS SHANGHAI/GSH2020LR Y083 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 60.0 Mpa |
| Bending stress | ISO178 | 105 Mpa | |
| Tensile modulus | ISO527-2 | 3300 Mpa | |
| Flexural modulus | ISO178 | 2800 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 4.6 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI GAS SHANGHAI/GSH2020LR Y083 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 3 |
| flammability | Test Condition | Test Method | MITSUBISHI GAS SHANGHAI/GSH2020LR Y083 |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI GAS SHANGHAI/GSH2020LR Y083 |
|---|---|---|---|
| Shrinkage rate | 吸水率(饱和,23°C) | 0.14 % | |
| MD:3.20mm | 0.30to0.50 % | ||
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 15.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ISO1133 | 17 g/10min |
| Shrinkage rate | TD:3.20mm | 0.30to0.50 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI GAS SHANGHAI/GSH2020LR Y083 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 132 °C |
| 1.8MPa,未退火 | ISO75-2/A | 131 °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 5E-05 cm/cm/°C |
| TD | ISO11359-2 | 5.9E-05 cm/cm/°C |