LDPE Trademark PE LD2923F Trademark Plastics Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
film | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LD2923F |
---|---|---|---|
Elmendorf tear strength | TD:51µm,吹塑薄膜 | ASTM D1922 | 200 g |
elongation | TD:断裂,51µm,吹塑薄膜 | ASTM D882 | 700 % |
tensile strength | TD:断裂,51µm,吹塑薄膜 | ASTM D882 | 18.6 MPa |
Secant modulus | 1%正割,MD:51µm,吹塑薄膜 | ASTM D882 | 172 MPa |
Elmendorf tear strength | MD:51µm,吹塑薄膜 | ASTM D1922 | 360 g |
Dart impact | 51µm,吹塑薄膜 | ASTM D1709 | 100 g |
film thickness | 51 µm | ||
Secant modulus | 1%正割,TD:51µm,吹塑薄膜 | ASTM D882 | 200 MPa |
elongation | MD:断裂,51µm,吹塑薄膜 | ASTM D882 | 350 % |
tensile strength | MD:断裂,51µm,吹塑薄膜 | ASTM D882 | 24.1 MPa |
optical performance | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LD2923F |
---|---|---|---|
Haze ratio | 50.8µm,吹塑薄膜 | ASTM D1003 | 5.0 % |
gloss | 45°,50.8µm,吹塑薄膜 | ASTM D2457 | 76 |
physical property | Test Condition | Test Method | Trademark Plastics Corporation/Trademark PE LD2923F |
---|---|---|---|
density | ASTM D1505 | 0.923 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.0 g/10min |