POM FL2010 MITSUBISHI ENGINEERING JAPAN
Iupital™ 
Fitness equipment
wear resistant,enhance,filling
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

machinabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2010
Dry conditions热风干燥 80℃---约3-4小时
Mold temperature60-80 °C
Processing temperature180-210 °C
Screw speed80-120 rpm
thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2010
Combustibility (rate)UL 94HB
Linear coefficient of thermal expansionASTM D696/ISO 113591.1E-04 mm/mm.℃
mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2010
Bending modulusASTM D790/ISO 1782400 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 17877 kg/cm²(MPa)[Lb/in²]
Elongation at BreakASTM D638/ISO 52718 %
Tensile modulusASTM D638/ISO 5272650 kg/cm²(MPa)[Lb/in²]
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2010
Arc resistanceASTM D495/IEC 60112600
Surface resistivityASTM D257/IEC 600931.E+16 Ω
Volume resistivityASTM D257/IEC 600931.E+12 Ω.cm
Physical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2010
densityASTM D792/ISO 11831.46
Shrinkage rateASTM D9552.0 %
Water absorption rateASTM D570/ISO 620.19 %