Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP E130i VF2201 TAIWAN POLYPLASTICS
LAPEROS®
Household appliances、Household appliances
heat-resisting、Flame retardant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i VF2201 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 31 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 43 kJ/m² |
| hardness | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i VF2201 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 71 |
| Mechanical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i VF2201 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 15000 Mpa | |
| bending strength | 23°C | ISO 178 | 220 Mpa |
| Compression Modulus | ISO 604 | 14000 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 13500 Mpa |
| Compressive Stress | 1%Strain | ISO 604 | 93.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 150 Mpa |
| Fracture bending strain | ISO 178 | 2.2 % | |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.6 % |
| Electrical performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i VF2201 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| relative permittivity | 2.05GHz | 内部方法 | 4.23 |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010 |
| arc resistance | 内部方法 | 140 sec | |
| Dissipation Factor | 2.05GHz | 内部方法 | 6E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.30 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.025 |
| flammability | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i VF2201 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 45 % |
| physical property | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i VF2201 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.40 % |
| MD | ISO 294-4 | 0.10 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.030 % |
| Thermal performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E130i VF2201 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 335 °C | |
| vicat | ISO 306/B50 | 195 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 276 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-06 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 216 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2E-05 cm/cm/°C |