| Impact resistance | Test Condition | Test Method | Chem Polymer Company/MDF2 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 55 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 15 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/A | 13 kJ/m² |
| Electrical performance | Test Condition | Test Method | Chem Polymer Company/MDF2 |
|---|---|---|---|
| dielectric strength | 3.00mm | IEC 60243-1 | 11 kV/mm |
| relative permittivity | IEC 60250 | 3.80 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Volume resistivity | IEC 60093 | 1E+17 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Mechanical properties | Test Condition | Test Method | Chem Polymer Company/MDF2 |
|---|---|---|---|
| tensile strength | ISO 527-2 | 180 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 4.0 % |
| Tensile modulus | ISO 527-2 | 8500 MPa | |
| Flexural modulus | ISO 178 | 7500 MPa | |
| bending strength | ISO 178 | 230 MPa |
| flammability | Test Condition | Test Method | Chem Polymer Company/MDF2 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 22 % |
| physical property | Test Condition | Test Method | Chem Polymer Company/MDF2 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.70to1.2 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.9 % |
| density | ISO 1183 | 1.37 g/cm³ |
| Thermal performance | Test Condition | Test Method | Chem Polymer Company/MDF2 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | >200 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |