Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PBT 310SEO-7001 SABIC INNOVATIVE THAILAND

LEXAN™

Industrial applications,switch,Shell,Electronic field,Electrical field

Flame retardant

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
Ball Pressure Test	H 358/30	ISO 2039-1	105 Mpa
Rockwell hardness	R -Sale	ISO 2039-2	120

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	74.0 °C
		0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	150 °C
		1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	60.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	73.0 °C
		0.45 MPa, Unannealed, 6.40 mm	ASTM D648	162 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	71.0 °C
Linear coefficient of thermal expansion	Flow : 60 to 138°C	ASTM E831	1.3E-4 cm/cm/°C
		Across Flow : -40°C	ISO 11359-2	7.3E-5 cm/cm/°C
		Across Flow : 23 to 60°C	ISO 11359-2	1.0E-4 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C
		Flow : -40 to 40°C	ISO 11359-2	7.6E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C
		Flow : 23 to 60°C	ISO 11359-2	1.0E-4 cm/cm/°C
RTI		UL 746	140 °C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C
thermal conductivity		ISO 8302	0.24 W/m/K
Vicat softening temperature	--	ASTM D152511	170 °C
Vicat softening temperature		--	ISO 306/A50	212 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
Bending modulus	--6	ISO 178	2600 Mpa
Bending modulus		50.0 mm Span5	ASTM D790	2620 Mpa
bending strength	--6,7	ISO 178	90.0 Mpa
bending strength		Yield, 50.0 mm Span5	ASTM D790	101 Mpa
elongation	Yield	ISO 527-2/50	5.0 %
		Yield4	ASTM D638	5.0 %
		Break4	ASTM D638	18 %
		Break	ISO 527-2/50	18 %
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	19.0 mg
Tensile modulus	--3	ASTM D638	2820 Mpa
Tensile modulus		--	ISO 527-2/1	2800 Mpa
tensile strength	Yield	ISO 527-2/50	58.0 Mpa
		Break	ISO 527-2/50	40.0 Mpa
		Break4	ASTM D638	52.0 Mpa
		Yield4	ASTM D638	58.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index	Solution B	IEC 60112	PLC 4
			UL 746	PLC 3
		--	IEC 60112	PLC 3
Dielectric strength	1.00 mm12	IEC 60243-1	18 KV/mm
		3.20 mm, in Oil	IEC 60243-1	17 KV/mm
		1.60 mm, in Oil	ASTM D149	24 KV/mm
		3.20 mm, in Air	ASTM D149	18 KV/mm
		0.800 mm, in Oil	IEC 60243-1	35 KV/mm
		1.60 mm, in Oil	IEC 60243-1	25 KV/mm
Dissipation factor	50 Hz	IEC 60250	1.0E-3
		60 Hz	IEC 60250	1.0E-3
		100 Hz	IEC 60250	2.0E-3
		1 MHz	IEC 60250	0.013
High arc combustion index		UL 746	PLC 0
High Voltage Arc Resistance Index (HVAR) (PLC)		UL 746	PLC 6
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 2
Relative permittivity	50 Hz	IEC 60250	2.90
		1 MHz	IEC 60250	2.80
		100 Hz	IEC 60250	3.10
		60 Hz	IEC 60250	2.90
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
melt mass-flow rate	250°C/2.16 kg	ASTM D1238	8.6 g/10 min
Melt Volume Flow Rate (MVR)	250°C/2.16 kg	ISO 1133	8.00 cm3/10min
Shrinkage rate	Flow : 0.750 to 2.30 mm	Internal Method	0.90 - 1.6 %
		Across FlowFlow : 2.30 to 4.60 mm	Internal Method	1.6 - 2.4 %
		Across FlowFlow : 0.750 to 2.30 mm	Internal Method	1.0 - 1.7 %
		Flow : 2.30 to 4.60 mm	Internal Method	1.5 - 2.3 %
		Flow 2	Internal Method	1.1 - 1.8 %
		Flow : 3.20 mm	Internal Method	1.5 - 2.3 %
		Across FlowFlow 2	Internal Method	0.90 - 1.9 %
Specific volume		ASTM D792	0.710 cm³/g
Water absorption rate	Saturation, 23°C	ISO 62	0.36 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.080 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
Dart impact	23°C, Total Energy	ASTM D3763	200 J
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C9	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength		23°C	ASTM D4812	无断裂

flammability	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	30 %
UL flame retardant rating	0.71 mm	UL 94	V-0
UL flame retardant rating		3.0 mm	UL 94	5VA

injection	Test Condition	Test Method	SABIC INNOVATIVE THAILAND/310SEO-7001
Back pressure			0.300 to 0.700 Mpa
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.013 to 0.025 mm
Mold temperature			50 to 75 °C
Processing (melt) temperature			245 to 260 °C
Screw speed			50 to 100 rpm
Spray nozzle temperature			240 to 255 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			245 to 260 °C
Temperature at the rear of the barrel			230 to 250 °C
Temperature in the middle of the barrel			240 to 255 °C

Get App