PC ML-3500ZEL TEIJIN JAPAN
PANLITE®
light-emitting diode,Lighting diffuser,Lighting applications
Light diffusion,Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3500ZEL |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 127 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| flame retardant performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3500ZEL |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-2 6.00mm | |
| UL -94 | V-2 0.40mm | ||
| UL -94 | V-2 1.50mm | ||
| UL -94 | V-2 3.00mm | ||
| UL -94 | V-2 0.75mm |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3500ZEL |
|---|---|---|---|
| flexural modulus | 23°C | ISO 178 | 95 Mpa |
| Elongation at break | 23°C | ISO 527-2 | >50 % |
| tensile strength | 23°C | ISO 527-2 | 57 Mpa |
| bending strength | 23°C | ISO 178 | 2130 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
| tensile strength | 屈服,23°C | ISO 527-2 | 61 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| Elongation at break | 屈服,23°C | ISO 527-2 | 6 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NB kJ/m² |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3500ZEL |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| volume resistivity | IEC 60093 | >1.0E+15 Ω.cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 Ω.cm |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3500ZEL |
|---|---|---|---|
| shrinkage rate | MD4.0mm | ISO 294-4 | 0.50-0.70 % |
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.20 % |
| melt mass-flow rate | 300℃/1.2Kg | ISO 1133 | 18.0 cm3/10min |
| shrinkage rate | TD4.0mm | ISO 294-4 | 0.50-0.70 % |