PA6T TKR4357G6 BASF GERMANY
Ultramid®
Automotive Applications、Engineering accessories
High rigidity、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/TKR4357G6 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃23°C | ISO 179 | 95 kJ/m² |
| Impact strength of cantilever beam gap | 23℃23℃ | ISO 180 | 23 kJ/m² |
| Charpy Notched Impact Strength | 23℃23°C | ISO 179 | 19 kJ/m² |
| Impact strength of simply supported beam without notch | -30℃-30°C | ISO 179 | 90 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/TKR4357G6 |
|---|---|---|---|
| tensile strength | 断裂，-40℃Break, -40°F | ISO 527-2 | 249 Mpa |
| 断裂，23℃Break, 73°F | ISO 527-2 | 165 Mpa | |
| Tensile strain | 断裂，23℃Break, 73°F | ISO 527-2 | 3.5 % |
| Tensile modulus | 23℃23℃ | ISO 527-2 | 9300 Mpa |
| Tensile strain | 断裂，-40℃Break, -40°F | ISO 527-2 | 3.6 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/TKR4357G6 |
|---|---|---|---|
| Dissipation Factor | 1 MHz1 MHz | IEC 60250 | 0.03 |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dielectric constant | 1 MHz1 MHz | IEC 60250 | 4.3 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Flame retardant performance | Test Condition | Test Method | BASF GERMANY/TKR4357G6 |
|---|---|---|---|
| UL flame retardant rating | 1.50 mm | UL 94 | HB |
| 0.75 mm | UL 94 | HB | |
| 3.00 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/TKR4357G6 |
|---|---|---|---|
| Water absorption rate | 饱和，23℃饱和，23℃ | ISO 62 | 4.5 % |
| 平衡，23℃，50% RH平衡，23℃，50% RH | ISO 62 | 0.8 % | |
| density | ISO 1183 | 1.37 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/TKR4357G6 |
|---|---|---|---|
| Electrical performance | 0.75 mm0.75 mm | UL 746 | 140 °C |
| 1.5 mm1.5 mm | UL 746 | 140 °C | |
| Linear coefficient of thermal expansion | TDTD | 0.000055 1/℃ | |
| MDMD | 0.000025 1/℃ | ||
| Impact mechanical performance | 0.75 mm0.75 mm | UL 746 | 100 °C |
| 3.0 mm3.0 mm | UL 746 | 115 °C | |
| tensile strength | 0.75 mm0.75 mm | UL 746 | 120 °C |
| Electrical performance | 3.0 mm3.0 mm | UL 746 | 140 °C |
| tensile strength | 3.0 mm3.0 mm | UL 746 | 140 °C |
| Heat distortion temperature | 1.8 MPa，未退火1.8 MPa，未退火，HDT | ISO 75-2/A | 240 °C |
| Impact mechanical performance | 1.5 mm1.5 mm | UL 746 | 110 °C |
| tensile strength | 1.5 mm1.5 mm | UL 746 | 140 °C |
| melting temperature | DSCDSC | ISO 3146 | 295 °C |