PA66 ASAHI JAPAN CR301

Injection grade

US$ 4,150 / MT

FOB Guangzhou port, China

thermal performance	Test Condition	Test Method	ASAHI JAPAN/CR301
Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	250 °C
		0.45 MPa, Unannealed	ISO 75-2/B	249 °C
		HDT	ASTM D648/ISO 75	191 ℃（℉）
		1.82MPa,干	ASTM D-648	191(250) °C
		1.8 MPa, Unannealed	ISO 75-2/A	188 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	4 mm/mm.℃
Linear coefficient of thermal expansion		Flow	ASTM D696	4.0E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	191 °C
Linear coefficient of thermal expansion	干	ASTM D-696	4 ×10-5/K
Combustibility (rate)		UL 94	HB
mechanical properties	Test Condition	Test Method	ASAHI JAPAN/CR301
elongation	Break	ASTM D638	3.0 %
Taber abraser	1000 Cycles	ASTM D1044	-- mg
Rockwell hardness	干(湿)	ASTM D-785	85(-) M Scale
bending strength	--	ASTM D790	147 Mpa
		23°C	ISO 178	140 Mpa
		干(湿)	ASTM D-790	147(93) Mpa
			ASTM D790/ISO 178	147(MPa) kg·cm/cm(J/M)ft·lb/in
tensile strength	干(湿)	ASTM D-638	88(64) Mpa
flexural coefficient	干(湿)	ASTM D-790	5.9(2.9) GPa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	34(39) J/m
Bending modulus	23°C	ISO 178	7400 Mpa
Rockwell hardness		ASTM D785	M85
Bending modulus	--	ASTM D790	5900 Mpa
Elongation at Break	干(湿)	ASTM D-638	3(3.5) %
tensile strength	Break, 23°C	ISO 527-2	85.0 Mpa
tensile strength		--	ASTM D638	88.0 Mpa
Tensile modulus	23°C	ISO 527-2	7000 Mpa
Bending modulus		ASTM D790/ISO 178	5880(MPa) kg·cm/cm(J/M)ft·lb/in
elongation	Break, 23°C	ISO 527-2	2.0 %
Physical properties	Test Condition	Test Method	ASAHI JAPAN/CR301
Water absorption rate		ASTM D570/ISO 62	1.5 %
Wear factor	湿	ASTM D-1044	8 ×10-6kg/1000times
Shrinkage rate	Flow	Internal Method	0.50 - 1.3 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	-- %
Water absorption rate		Saturation, 23°C		-- %
Shrinkage rate	干	旭化成方法	0.5-1.3 %
Shrinkage rate			ASTM D955	0.5-1.3 %
density		ASTM D792/ISO 1183	1.48
other	Test Condition	Test Method	ASAHI JAPAN/CR301
characteristic			电气特性
purpose			自动车电装部件
Electrical performance	Test Condition	Test Method	ASAHI JAPAN/CR301
Arc resistance		ASTM D495/IEC 60112	150
flammability	Test Condition	Test Method	ASAHI JAPAN/CR301
UL flame retardant rating	0.75 mm	UL 94	HB
Basic Performance	Test Condition	Test Method	ASAHI JAPAN/CR301
Water absorption rate	湿		1.5 %
impact performance	Test Condition	Test Method	ASAHI JAPAN/CR301
Impact strength of simply supported beam without notch		ISO 179	51 kJ/m²
hardness	Test Condition	Test Method	ASAHI JAPAN/CR301
Rockwell hardness	M -Sale	ISO 2039-2	85
Rockwell hardness		M-Scale	ASTM D785	85