Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA6 Sup-tech B706 Shanghai Suptech Engineering Plastics Co. Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B706 |
---|---|---|---|
Charpy Notched Impact Strength | DIN 53453 | 13 kJ/m² |
hardness | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B706 |
---|---|---|---|
Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
Electrical performance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B706 |
---|---|---|---|
dielectric strength | DIN 53481 | 20 kV/mm | |
Surface Resistivity | IEC 60093 | 1E+12 ohms |
Mechanical properties | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B706 |
---|---|---|---|
Tensile strain | 断裂 | DIN 53452 | 2.0 % |
tensile strength | 断裂 | DIN 53455 | 170 MPa |
Flexural modulus | DIN 53457 | 7500 MPa | |
bending strength | DIN 53457 | 230 MPa |
flammability | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B706 |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B706 |
---|---|---|---|
density | DIN 53479 | 1.36 g/cm³ | |
Shrinkage rate | DIN 53464 | 1.5E-3-5.0E-3 % | |
Water absorption rate | 饱和,23°C | DIN 53495 | 5.5 % |
23°C,24hr | DIN 53495 | 1.1 % |
Thermal performance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B706 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | DIN 53461 | 205 °C |
0.45MPa,未退火,HDT | DIN 53461 | 220 °C |