Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF-3200H Samsung Cheil South Korea
INFINO®
Automotive components、Home appliance components
High temperature resistan、UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/Samsung Cheil South Korea/HF-3200H
Ash Content
ISO3451
%
1
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt mass flow rate
250°C/10.0kg
ASTMD1238
g/10min
1
Melt mass flow rate
250°C/10.0kg
ISO1133
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
PC/Samsung Cheil South Korea/HF-3200H
CharpyNotchedImpactStrength
23°C
ISO179/1eA
kJ/m²
1
Tensile modulus
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/50
Mpa
5
tensile strength
屈服
ASTMD638
Mpa
7
tensile strength
屈服
ISO527-2/50
Mpa
1
tensile strength
断裂
ASTMD638
Mpa
1
tensile strength
断裂
ISO527-2/50
Mpa
1
elongation
断裂
ASTMD638
%
4
elongation
断裂
ISO527-2/50
%
3
Bending modulus
ASTMD790
Mpa
4
Bending modulus
ISO178
Mpa
5
Bending strength
ASTMD790
Mpa
1
bending strength
ISO178
Mpa
1
Impact strength of cantilever beam gap
23°C,3.18mm
ASTMD256
J/m
1
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
PC/Samsung Cheil South Korea/HF-3200H
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
1
Hot deformation temperature
0.45MPa,Annealed,4.00mm
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
1
Hot deformation temperature
1.8MPa,Annealed,4.00mm
ISO75-2/A
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1