POM F40-03 MITSUBISHI THAILAND
Iupital™ 
Thin walled components
High mobility、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/F40-03
Impact strength of simply supported beam without notch23°CISO 179100 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/F40-03
Tensile modulusISO 527-22900 Mpa
Nominal tensile fracture strainISO 527-220 %
bending strengthISO 17891.0 Mpa
Flexural modulusISO 1782700 Mpa
Tensile strain屈服ISO 527-27.0 %
tensile strength 屈服ISO 527-264.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/F40-03
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
dielectric strength1.00mmIEC 60243-132 KV/mm
Volume resistivityIEC 600931E+14 ohms·cm
Dissipation Factor100HzIEC 602502E-03
relative permittivity100HzIEC 602503.90
dielectric strength3.00mmIEC 60243-119 KV/mm
relative permittivity1MHzIEC 602503.90
Surface ResistivityIEC 600931E+16 ohms
Dissipation Factor1MHzIEC 602507E-03
flammabilityTest ConditionTest MethodMITSUBISHI THAILAND/F40-03
UL flame retardant rating0.8mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI THAILAND/F40-03
Melt volume flow rate190°C/2.16kgISO 113345.0 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.22 %
Shrinkage rateMD：3.00mm2.0 %
melt mass-flow rate190°C/2.16kgISO 113352 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/F40-03
melting temperatureISO 11357-3166 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B156 °C
1.8MPa,未退火，HDTISO 75-2/A100 °C
Linear coefficient of thermal expansionMDISO 11359-21.1E-04 cm/cm/°C
TDISO 11359-21.1E-04 cm/cm/°C