PPO 100Z ASAHI JAPAN
XYRON™
Fitness equipment、Sports Equipment
Chemical resistance、Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 16 kJ/m² |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.50-0.70 % | |
| Water absorption rate | ASTM D-570 | 0.10 % | |
| density | ASTM D-792 | 1.08 g/cm |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 59 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2250 kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 2350 Mpa | ||
| bending strength | ASTM D-790 | 59 Mpa | |
| tensile strength | ASTM D-638 | 39 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 40 % | |
| Rockwell hardness | ASTM D785 | R110 | |
| tensile strength | ASTM D638/ISO 527 | 36 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 23°C | ISO 178 | 66.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 37.0 Mpa |
| UL flame retardant rating | UL 94 | V-0 | |
| Flexural modulus | 23°C | ISO 178 | 2370 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 30 % |
| elongation at break | ASTM D-638 | 40 % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 2.90 |
| Dissipation Factor | 100Hz | IEC 60250 | 3E-03 |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| dielectric constant | 1MHz | IEC 60250 | 2.90 |
| dielectric strength | 2.00mm | IEC 60243-1 | 29 KV/mm |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 4E-03 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.08 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.1 % |
| processability | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| Temperature | 40-70 °C |
| flammability | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/100Z |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 °C |
| HDT | ASTM D648/ISO 75 | 85 ℃（℉） | |
| Linear coefficient of thermal expansion | MD：-30到65°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 78.0 °C |