Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 503R-BL2G029 SABIC INNOVATIVE US
LEXAN™
fibre
High impact resistance、High rigidity、Glass fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/503R-BL2G029 |
|---|---|---|---|
| Vicat Softening Temperature | ASTMD15255 | 154 °C | |
| Specific Heat | ASTMC351 | 1210 J/kg/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 142 °C |
| RTIElec | UL746 | 120 °C | |
| Thermal Conductivity | ASTMC177 | 0.20 W/m/K | |
| RTIStr | UL746 | 125 °C | |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 3.2E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 110 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 146 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/503R-BL2G029 |
|---|---|---|---|
| Rockwell Hardness | M计秤 | ASTMD785 | 85 |
| R计秤 | ASTMD785 | 124 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/503R-BL2G029 |
|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.12 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.40 % |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 0.31 % |
| Specific Volume | ASTMD792 | 0.802 cm³/g | |
| Outdoor Suitability | UL746C | f1 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/503R-BL2G029 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 3450 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 103 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 8.0 % |
| 断裂 | ASTMD638 | 15 % | |
| Tensile Strength | 屈服 | ASTMD638 | 66.2 Mpa |
| 断裂 | ASTMD638 | 55.2 Mpa | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 11.0 mg |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/503R-BL2G029 |
|---|---|---|---|
| Gardner Impact | 23°C | ASTMD3029 | 102 J |
| Tensile Impact Strength | ASTMD1822 | 158 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/503R-BL2G029 |
|---|---|---|---|
| Oxygen Index | ASTMD2863 | 36 % | |
| Flame Rating | 3.0mm | UL94 | 5VA |
| 1.5mm | UL94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/503R-BL2G029 |
|---|---|---|---|
| Dissipation Factor? | 50Hz | ASTMD150 | 8E-04 |
| 60Hz | ASTMD150 | 8E-04 | |
| 1MHz | ASTMD150 | 7.5E-03 | |
| Hot-wire Ignition | HWI | UL746 | PLC 1 |
| High Amp Arc Ignition | HAI | UL746 | PLC 1 |
| Volume Resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| Dielectric Constant | 60Hz | ASTMD150 | 3.10 |
| 50Hz | ASTMD150 | 3.10 | |
| 1MHz | ASTMD150 | 3.05 | |
| Arc Resistance | ASTMD495 | PLC7 | |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 18 KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC 4 |