Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3W BK BASF GERMANY
Ultramid®
wheel,Engine parts,Laptop case,bearing
Oil resistant,Fast forming cycle,High mobility,heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/A3W BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.6 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 48 J/m |
| 23°C | ASTM D256 | 53 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 4.5 kJ/m² |
| -40°C | ISO 180 | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3W BK |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2 | 88.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.7 % |
| Flexural modulus | 23°C | ISO 178 | 3100 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 3300 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 85.0 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 4.5 % |
| flammability | Test Condition | Test Method | BASF GERMANY/A3W BK |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 3.0mm | UL 94 | V-2 | |
| 6.0mm | UL 94 | V-2 | |
| 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | BASF GERMANY/A3W BK |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 8.5 % |
| 平衡,50%RH | ASTM D570 | 2.8 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.8 % | |
| 饱和,23°C | ISO 62 | 8.5 % | |
| density | ASTM D792 | 1.14 g/cm³ | |
| ISO 1183 | 1.14 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/A3W BK |
|---|---|---|---|
| RTI Elec | 6.0mm | UL 746 | 130 °C |
| RTI Str | 0.75mm | UL 746 | 105 °C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| RTI Str | 6.0mm | UL 746 | 110 °C |
| melting temperature | ASTM D3418 | 260 °C | |
| RTI Elec | 3.0mm | UL 746 | 130 °C |
| RTI Imp | 3.0mm | UL 746 | 105 °C |
| melting temperature | ISO 3146 | 260 °C | |
| RTI Elec | 0.75mm | UL 746 | 130 °C |
| RTI Imp | 0.75mm | UL 746 | 105 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| RTI Str | 1.5mm | UL 746 | 105 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C |
| RTI Str | 3.0mm | UL 746 | 110 °C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| RTI Imp | 6.0mm | UL 746 | 105 °C |