PBT 1184G-15 TORAY JAPAN
Toraycon®
Electrical components
Flame retardant,Glass fiber reinforced,High toughness
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/1184G-15 |
|---|---|---|---|
| arc resistance | ASTM D495 | 133 S | |
| dielectric constant | 50Hz | ASTM D150 | 3.6 |
| Dielectric loss | 10，正切 | ASTM D150 | 0.02 |
| dielectric strength | ASTM D149 | 25 MV/m | |
| dielectric constant | ASTM D150/IEC 60250 | 3.8 | |
| 10 | ASTM D150 | 3.8 | |
| Dielectric loss | 50Hz，正切 | ASTM D150 | 0.002 |
| Volume resistivity | ASTM D257/IEC 60093 | 3.0x10^14 Ω.cm | |
| ASTM D257 | 3.0 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1184G-15 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 50 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 150 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 5600 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 87 M | |
| elongation at break | ASTM D638/ISO 527 | 5 % | |
| Rockwell hardness | ASTM D785 | M87 | |
| bending strength | 23℃ | ASTM D790 | 150 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 5.6 GPa |
| tensile strength | ASTM D638/ISO 527 | 110 kg/cm²(MPa)[Lb/in²] | |
| coefficient of friction | 对本身 | ASTM D1894 | 0.20 |
| elongation | 23℃ | ASTM D638 | 5 % |
| tensile strength | 23℃ | ASTM D638 | 110 Mpa |
| Impact strength of cantilever beam gap | 缺口，23℃ | ASTM D256 | 60 J/m |
| coefficient of friction | 对金属 | ASTM D1894 | 0.15 |
| Impact strength of cantilever beam gap | 无缺口，23℃ | ASTM D256 | 50 KJ/m |
| other | Test Condition | Test Method | TORAY JAPAN/1184G-15 |
|---|---|---|---|
| characteristic | 增强阻燃等级.V-0.15%玻纤增强 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/1184G-15 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.56 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| physical property | Test Condition | Test Method | TORAY JAPAN/1184G-15 |
|---|---|---|---|
| Water absorption rate | 23℃,24hr | ASTM D570 | 0.07 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1184G-15 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 200 ℃（℉） |
| 0.45MPa，HDT | ASTM D648 | 215 °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 5.3x10^-5 mm/mm.℃ | |
| Heat distortion temperature | 1.82Mpa，HDT | ASTM D648 | 200 °C |
| Linear coefficient of thermal expansion | ASTM D696 | 5.3 | |
| UL flame retardant rating | UL 94 | V-0 |