PA66 HTN52G30NH DUPONT USA
Zytel®
Automotive sector,Electrical appliances,Electronic field,Electrical field
High temperature resistan,Flame retardant,Thermal stability,Glass fiber reinforced,30% glass fiber reinforce,Flame retardant,High lubrication performa
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | DUPONT USA/HTN52G30NH |
|---|---|---|---|
| Hot deformation temperature | HDT | ISO 75-2/B | 300 °C |
| HDT | ISO 75-2/A | 282 °C | |
| HDT | ASTM D790/ISO 178 | 285 °C | |
| Melting temperature | ISO 11357-1/-3 | 310 °C | |
| UL flame retardant rating | UL 94 | V-0 |
| mechanical properties | Test Condition | Test Method | DUPONT USA/HTN52G30NH |
|---|---|---|---|
| Bending modulus | ISO 178 | 8900 Mpa | |
| ASTM D790 | 11400 Mpa | ||
| bending strength | ISO 178 | 238 Mpa | |
| ASTM D790 | 240 Mpa | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 11 kJ/m² | |
| elongation | ASTM D638 | 2.0 % | |
| Fracture strain | ISO 527 | 2.0 % | |
| Fracture stress | ISO 527 | 145 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 115 J/m | |
| Tensile modulus | ISO 527-2 | 13000 Mpa | |
| ISO 527 | 10000 Mpa | ||
| tensile strength | ISO 527-2 | 150 Mpa |
| Physical properties | Test Condition | Test Method | DUPONT USA/HTN52G30NH |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.30 % |
| TD | ISO 294-4 | 0.60 % |