POM Copolymer BESTPOM C09H08/01 TRIESA SPAIN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TRIESA SPAIN/BESTPOM C09H08/01 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 75 kJ/m² |
| hardness | Test Condition | Test Method | TRIESA SPAIN/BESTPOM C09H08/01 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 81 |
| Electrical performance | Test Condition | Test Method | TRIESA SPAIN/BESTPOM C09H08/01 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 19 kV/mm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| Mechanical properties | Test Condition | Test Method | TRIESA SPAIN/BESTPOM C09H08/01 |
|---|---|---|---|
| tensile strength | ISO 527-2 | 64.0 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 30 % |
| Tensile modulus | ISO 527-2 | 2900 MPa |
| flammability | Test Condition | Test Method | TRIESA SPAIN/BESTPOM C09H08/01 |
|---|---|---|---|
| burning rate | FMVSS302 | <100 mm/min | |
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TRIESA SPAIN/BESTPOM C09H08/01 |
|---|---|---|---|
| humidity | 颗粒 | ISO 1110 | 0.20 % |
| melt mass-flow rate | ISO 1133 | 9.0 g/10min | |
| Shrinkage rate | ISO 294-4 | 2.0 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| density | ISO 1183 | 1.42 g/cm³ |
| Thermal performance | Test Condition | Test Method | TRIESA SPAIN/BESTPOM C09H08/01 |
|---|---|---|---|
| vicat | ISO 306 | 165 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 110 °C |