Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 3025N2 I(R) 3056D SAMYANG SHANHAI
TRIREX®
Laptop case,Electronic and Electrical Applications,Plastic toy,Lighting applications
Dimensional stability,Low water absorption
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SAMYANG SHANHAI/3025N2 I(R) 3056D |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 122 |
| Mechanical properties | Test Condition | Test Method | SAMYANG SHANHAI/3025N2 I(R) 3056D |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 120 % |
| bending strength | 屈服 | ASTM D790 | 88.3 Mpa |
| tensile strength | 屈服 | ASTM D638 | 68.6 Mpa |
| Flexural modulus | ASTM D790 | 2160 Mpa |
| Electrical performance | Test Condition | Test Method | SAMYANG SHANHAI/3025N2 I(R) 3056D |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 4E+16 ohms·cm | |
| Dissipation Factor | ASTM D150 | 8.2E-03 | |
| dielectric strength | ASTM D149 | 30 KV/mm | |
| dielectric constant | ASTM D150 | 2.80 | |
| arc resistance | ASTM D495 | 90.0 sec |
| flammability | Test Condition | Test Method | SAMYANG SHANHAI/3025N2 I(R) 3056D |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SAMYANG SHANHAI/3025N2 I(R) 3056D |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | SAMYANG SHANHAI/3025N2 I(R) 3056D |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 133 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 144 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 5.5E-05 cm/cm/°C |