TSU Innothane® IE-60DC Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | Innovative Polymers, Inc./Innothane® IE-60DC |
|---|---|---|---|
| PeakExotherm | 49 °C |
| Mechanical properties | Test Condition | Test Method | Innovative Polymers, Inc./Innothane® IE-60DC |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 103 MPa |
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./Innothane® IE-60DC |
|---|---|---|---|
| Thermosetting components | 脱模时间 | 120to240 min | |
| 硬化法 | 按重量计算的混合比:12按容量计算的混合比:13 | ||
| 树脂 | 按重量计算的混合比:100按容量计算的混合比:100 |
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./Innothane® IE-60DC |
|---|---|---|---|
| Viscosity | 固化时间(25°C) | 24 hr | |
| 25°C4 | 2.8 Pa·s | ||
| GelTime | 9.0to13 min | ||
| 25°C2 | 0.25 Pa·s | ||
| 25°C3 | 2.2 Pa·s |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./Innothane® IE-60DC |
|---|---|---|---|
| tear strength | ASTM D624 | 36.8 kN/m | |
| Shore hardness | ShoreD | ASTM D2240 | 35to45 |
| elongation | 断裂 | ASTM D638 | 190 % |
| tensile strength | ASTM D638 | 11.9 MPa |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./Innothane® IE-60DC |
|---|---|---|---|
| density | Hardener | 1.06 g/cm³ | |
| 基体树脂 | 1.12 g/cm³ | ||
| Cured | 1.10 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 0.020 % |
| Thermal performance | Test Condition | Test Method | Innovative Polymers, Inc./Innothane® IE-60DC |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 60.0 °C |