Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 0309 CELANESE USA
--
fibre
heat-resisting、Chemical resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/0309 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 93 |
| M级 | ISO 2039-2 | 90 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/0309 |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 1E-03 |
| Volume resistivity | ASTM D257 | 1E+07 ohms·cm | |
| dielectric strength | IEC 60243-1 | 18 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+11 ohms·cm | |
| dielectric constant | 1kHz | ASTM D150 | 3.00 |
| Dissipation Factor | 1MHz | ASTM D150 | 9E-04 |
| dielectric strength | ASTM D149 | 18 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| relative permittivity | 1MHz | IEC 60250 | 4.60 |
| Dissipation Factor | 1MHz | IEC 60250 | 1.1E-03 |
| arc resistance | ASTM D495 | 124 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/0309 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 145 Mpa |
| Flexural modulus | 23°C | ISO 178 | 4200 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 90.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 8.0 % |
| physical property | Test Condition | Test Method | CELANESE USA/0309 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.0-1.2 % |
| SpecificHeatCapacity of Melt | 内部方法 | 1830 J/kg/°C | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.020 % |
| Shrinkage rate | TD | ASTM D955 | 0.80-1.0 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/0309 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 104 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 115 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 204 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 95.0 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 5.3E-05 cm/cm/°C |
| Glass Transition Temperature | ISO 11357-2 | 90.0 °C |