Product Name
Brand Name
Usages
Properties
Certificates
PBT 315-1001 SABIC INNOVATIVE NETHERLANDS
VALOX™
Automotive Applications、Electrical applications、currency
Glass fiber reinforced、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/315-1001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/315-1001 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 117 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/315-1001 |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.90 |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 29 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 2.90 |
| 100Hz | IEC 60250 | 3.30 | |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 15 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.40 |
| Dissipation Factor | 50Hz | IEC 60250 | 3E-04 |
| 60Hz | IEC 60250 | 3E-04 | |
| 1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | V |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | V |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 24 KV/mm |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/315-1001 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| bending strength | ISO 178 | 75.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| 屈服 | ISO 527-2/50 | 3.5 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 30.0 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/315-1001 |
|---|---|---|---|
| Burning wire flammability index | 2.02mm | IEC 60695-2-12 | 960 °C |
| 1.00mm | IEC 60695-2-12 | 850 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/315-1001 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.1-1.8 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| Melt volume flow rate | 250°C/1.2kg | ISO 1133 | 6.00 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.34 % |
| Shrinkage rate | TD | 内部方法 | 0.90-1.8 % |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 9.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/315-1001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 120 °C | |
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 55.0 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |