Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 910-X01 TORAY JAPAN
Toyolac®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/910-X01 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 13 % |
| bending strength | 23°C | ISO 178 | 85.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 57.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2630 Mpa |
| optical performance | Test Condition | Test Method | TORAY JAPAN/910-X01 |
|---|---|---|---|
| Haze ratio | 3000µm | ISO 14782 | 3.0 % |
| transmissivity | 总计,3000µm | ISO 13468 | 87.0 % |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/910-X01 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.10 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 28 g/10min |
| flammability | Test Condition | Test Method | TORAY JAPAN/910-X01 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/910-X01 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.40-0.60 % | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 28 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/910-X01 |
|---|---|---|---|
| vicat | 85.0to90.0 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 78.0 °C |