Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 TS150F3A Nature 浙江新力
--
高流动性,高韧性,耐热好,高阻燃
接插件,接线端子
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 浙江新力/TS150F3A Nature |
|---|---|---|---|
| Tensile strength at break | IS0527 | 70 Mpa | |
| Yield bending strength | IS0178 | 100 Mpa | |
| Flexural modulus | IS0178 | 3000 Mpa | |
| elongation at break | IS0527 | 10 % | |
| Impact strength of simply supported beam without notch | IS0179 | kJ/m² | |
| Charpy Notched Impact Strength | IS0179 | 5.0 kJ/m² |
| other | Test Condition | Test Method | 浙江新力/TS150F3A Nature |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.00E+14 Ω | |
| proof tracking index | IEC 60112 | 600 3mm/v | |
| Linear forming shrinkage rate | IS02577 | 1.0 % |
| Flame retardant performance | Test Condition | Test Method | 浙江新力/TS150F3A Nature |
|---|---|---|---|
| Flame retardant performance | 厚度3.0mm | UL 94 | ℃ |
| 厚度1.5mm | UL94 | ℃ | |
| 厚度2.0mm | UL94 | ℃ | |
| 厚度0.8mm | UL94 | V-0 ℃ |
| physical property | Test Condition | Test Method | 浙江新力/TS150F3A Nature |
|---|---|---|---|
| density | IS01183 | 1.16 g/cm | |
| Water absorption rate | IS062 | 2.0 % |
| Thermal performance | Test Condition | Test Method | 浙江新力/TS150F3A Nature |
|---|---|---|---|
| Hot deformation temperature 1.8MPa | IS076 | ℃ | |
| Hot deformation temperature 0.45MPa | IS076 | 230 ℃ | |
| GWFI | 厚度1.5mm | IEC 60695-2-12 | ℃ |
| 厚度0.8mm | IEC 60695-2-12 | 960 ℃ | |
| 厚度3.0mm | IEC 60695-2-11 | ℃ | |
| GWIT | 厚度0.8mm | IEC 60695-2-13 | 750 ℃ |
| GWFI | 厚度2.0mm | IEC 60695-2-12 | ℃ |