Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MS TX-100K DENKA JAPAN
--
Casters
Weather resistance、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/TX-100K |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 115 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 3400 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 85 |
| optical performance | Test Condition | Test Method | DENKA JAPAN/TX-100K |
|---|---|---|---|
| Total Light Transmittance | 2mmt | ISO 13456-1 | 92 % |
| tortuosity | Na-D线 | ASTM D542 | 1.53 |
| Haze ratio | 2mmt | JIS K7130 | 0.2 % |
| Physical properties | Test Condition | Test Method | DENKA JAPAN/TX-100K |
|---|---|---|---|
| density | 1.132 |
| physical property | Test Condition | Test Method | DENKA JAPAN/TX-100K |
|---|---|---|---|
| Tensile strain | 50mm/min，断裂 | ISO 527-2 | 10 % |
| Rockwell hardness | ISO 2038-2 | M | 85 |
| bending strength | 2mm/min | ISO 178 | 115 Mpa |
| Charpy Notched Impact Strength | 23℃ 有缺口 | ISO 178 | 2 kJ/m² |
| Tensile stress | 50mm/min，断裂 | ISO 527-1 | 67 Mpa |
| melt mass-flow rate | 200℃ 48N荷重 | ISO 1133 | 1.2 g/10min |
| Flexural modulus | 2mm/min | ISO 178 | 3400 Mpa |
| Heat distortion temperature | 平面方向1.8MPa应力 | ISO 75-1 | 79 °C |
| vicat | 50N荷重 | ISO 306 | 101 °C |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/TX-100K |
|---|---|---|---|
| vicat | ASTM D1525/ISO R306 | 101 ℃（℉） |