PPA HFFR 4133NT SOLVAY USA
AMODEL®
Automotive Applications、Laptop case、Electrical/Electronic App
Low warpage、Glass fiber reinforced、Filler: Glass fiber reinf、33% filler by weight、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/HFFR 4133NT |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 7.0to8.0 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 40to48 kJ/m² |
| hardness | Test Condition | Test Method | SOLVAY USA/HFFR 4133NT |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 121 |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/HFFR 4133NT |
|---|---|---|---|
| Dissipation Factor | 100Hz | ASTM D150 | 5E-03 |
| Volume resistivity | ASTM D257 | 1.3E+16 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.012 |
| dielectric constant | 1MHz | ASTM D150 | 3.53 |
| dielectric strength | 1.60mm | ASTM D149 | 26 KV/mm |
| dielectric constant | 100Hz | ASTM D150 | 3.78 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| dielectric strength | 0.800mm | ASTM D149 | 30 KV/mm |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/HFFR 4133NT |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 12000 Mpa | |
| bending strength | ISO 178 | 220to230 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.9to2.3 % |
| Flexural modulus | ISO 178 | 10800 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 145to160 Mpa |
| flammability | Test Condition | Test Method | SOLVAY USA/HFFR 4133NT |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SOLVAY USA/HFFR 4133NT |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.3 % |
| MD | ISO 294-4 | 0.32 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.28 % |
| density | ISO 1183/A | 1.46 g/cm³ |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/HFFR 4133NT |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 300 °C |
| Linear coefficient of thermal expansion | MD:120到200°C | ASTME831 | 1.2E-05 cm/cm/°C |
| MD:0到90°C | ASTME831 | 2E-05 cm/cm/°C | |
| TD:0到90°C | ASTME831 | 8E-05 cm/cm/°C | |
| TD:120到200°C | ASTME831 | 1.3E-04 cm/cm/°C |