PP F327BV PRIME POLYMER JAPAN
PRIME POLYPRO
film
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PRIME POLYMER JAPAN/F327BV |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 12 kJ/m² |
| hardness | Test Condition | Test Method | PRIME POLYMER JAPAN/F327BV |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 85 |
| Basic performance | Test Condition | Test Method | PRIME POLYMER JAPAN/F327BV |
|---|---|---|---|
| melt mass-flow rate | 230℃ | ISO 1133 | 7 g/10min |
| density | ISO 1183 | 0.910 g/cm³ |
| Mechanical properties | Test Condition | Test Method | PRIME POLYMER JAPAN/F327BV |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 850 Mpa | |
| tensile strength | ISO 527 | 23 Mpa | |
| elongation | ISO 527 | 200 | |
| Impact strength of cantilever beam gap | 23℃ | ISO 179 | 12 kJ/m² |
| Tensile strain | 断裂 | ISO 527-2 | >200 % |
| Shore hardness | R-Scale | ISO 2039-2 | 85 |
| tensile strength | 屈服 | ISO 527-2 | 23.0 Mpa |
| Load resistant bending temperature | ISO 75 | 80 °C |
| physical property | Test Condition | Test Method | PRIME POLYMER JAPAN/F327BV |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | PRIME POLYMER JAPAN/F327BV |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 80.0 °C |