PPS PPS-hMR60 SICHUAN DEYANG
--
Laptop case、Automotive sector、High temperature applicat、bolt、Casters
filling、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | SICHUAN DEYANG/PPS-hMR60 |
|---|---|---|---|
| density | 1.94 g/cm |
| Mechanical properties | Test Condition | Test Method | SICHUAN DEYANG/PPS-hMR60 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 176 kg/cm²(MPa)[Lb/in²] | |
| compressive strength | 160 Mpa | ||
| Flexural modulus | ASTM D790/ISO 178 | 1.54*10^4 kg/cm²(MPa)[Lb/in²] | |
| 1.63×10 Mpa | |||
| Rockwell hardness | 96 | ||
| bending strength | 244 Mpa | ||
| Impact strength of cantilever beam gap | 12 KJ/m | ||
| elongation at break | ASTM D638/ISO 527 | 1.3 % | |
| tensile strength | 164 Mpa | ||
| Rockwell hardness | ASTM D785 | 110 | |
| tensile strength | ASTM D638/ISO 527 | 172 kg/cm²(MPa)[Lb/in²] | |
| elongation | 断裂 | 2.5 % |
| Electrical performance | Test Condition | Test Method | SICHUAN DEYANG/PPS-hMR60 |
|---|---|---|---|
| dielectric constant | 1MHz | 5.0 | |
| Dielectric loss | 1MHz | 0.010 | |
| Volume resistivity | 8×10 Ω.m | ||
| Surface Resistivity | 3×10 Ω | ||
| dielectric strength | 14 KV/mm | ||
| Compared to the Leakage Tracking Index (CTI) | PLC 4 |
| Physical properties | Test Condition | Test Method | SICHUAN DEYANG/PPS-hMR60 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.25/0.75 % | |
| density | ASTM D792/ISO 1183 | 1.92 |
| physical property | Test Condition | Test Method | SICHUAN DEYANG/PPS-hMR60 |
|---|---|---|---|
| Shrinkage rate | 平行 | 0.25 % | |
| 垂直 | 0.75 % |
| Thermal performance | Test Condition | Test Method | SICHUAN DEYANG/PPS-hMR60 |
|---|---|---|---|
| Heat distortion temperature | HDT | 270 °C | |
| melting temperature | 288 °C | ||
| UL flame retardant rating | UL -94 | V-0 |