PBT LONGLITE® PBT 6015-104X Chang Chun Plastics Co., Ltd. (CCP Group)
--
--
Filler, glass fiber reinforced material, 15%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodChang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 6015-104X
Charpy Notched Impact Strength23°CISO 179/1eA7.0 kJ/m²
Mechanical propertiesTest ConditionTest MethodChang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 6015-104X
Flexural modulus23°CISO 1784500 MPa
Tensile strain断裂,23°CISO 527-22.5 %
Tensile modulus23°CISO 527-25500 MPa
tensile strength 断裂,23°CISO 527-295.0 MPa
bending strength23°CISO 178140 MPa
Electrical performanceTest ConditionTest MethodChang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 6015-104X
Volume resistivityIEC 600931E+14 ohms·cm
dielectric strength2.00mmIEC 60243-124 kV/mm
Surface ResistivityIEC 600931E+13 ohms
flammabilityTest ConditionTest MethodChang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 6015-104X
UL flame retardant ratingUL 94HB
physical property Test ConditionTest MethodChang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 6015-104X
melt mass-flow rate250°C/2.16kgISO 113316 g/10min
Shrinkage rateTDISO 294-40.50to0.90 %
MDISO 294-40.20to0.60 %
densityISO 11831.36 g/cm³
Thermal performanceTest ConditionTest MethodChang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 6015-104X
melting temperatureISO 11357-3225 °C
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B170 °C
1.8MPa,未退火,HDTISO 75-2/A130 °C