Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PMMI TT50 Altuglas International of Arkema Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Altuglas International of Arkema Inc./ TT50 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 20 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Altuglas International of Arkema Inc./ TT50 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/5 | 80.0 MPa |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.0 % |
| Tensile modulus | ISO 527-2/1 | 4000 MPa |
| optical performance | Test Condition | Test Method | Altuglas International of Arkema Inc./ TT50 |
|---|---|---|---|
| transmissivity | ISO 13468-2 | 91.0 % | |
| refractive index | ISO 489 | 1.530 |
| flammability | Test Condition | Test Method | Altuglas International of Arkema Inc./ TT50 |
|---|---|---|---|
| UL flame retardant rating | DIN 4102 | B2 | |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Altuglas International of Arkema Inc./ TT50 |
|---|---|---|---|
| Melt volume flow rate | 260°C/10.0kg | ISO 1133 | 5.00 cm³/10min |
| density | ISO 1183 | 1.21 g/cm³ |
| Thermal performance | Test Condition | Test Method | Altuglas International of Arkema Inc./ TT50 |
|---|---|---|---|
| Glass Transition Temperature | IEC 1006 | 151 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 140 °C |
| vicat | ISO 306/B50 | 150 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 132 °C |
| Linear coefficient of thermal expansion | MD：0到50°C | ISO 11359-2 | 5.3E-05 cm/cm/°C |